Home About us Contact
|
Home About us Contact | ||
|
|
||
Self-etching System (self-etching + system)
Selected AbstractsEffect of post-space treatment on retention of fiber posts in different root regions using two self-etching systemsEUROPEAN JOURNAL OF ORAL SCIENCES, Issue 3 2008Ling Zhang The effect of post-space treatment on the retention of fiber posts in different root regions was evaluated using two self-etching systems. Post spaces were prepared in extracted premolars and then the root canals were subjected to one of the following post-space treatments: (i) water irrigation (control); (ii) etching with 35% phosphoric acid for 30 s; (iii) irrigation with 17% EDTA followed by 5.25% sodium hypochlorite (NaOCl); and (iv) ultrasonic agitation associated with 17% EDTA and 5.25% NaOCl irrigating solutions. The dentin surfaces were examined under scanning electron microscopy (SEM) after different post-space treatments. Fiber posts were then luted in the treated roots using resin cement with either Clearfil SE Bond or Clearfil DC Bond, and the thin-slice push-out test was performed. Scanning electron microscopy showed that all the post-space treatments tested were effective in removal of the smear layer of debris, or sealer/gutta-percha remnants, on the root canal. The apical push-out strength was affected by post-space treatment. Both 35% phosphoric acid etching and ultrasonic agitation in combination with EDTA/NaOCl irrigation improved the apical push-out strength of the fiber post, regardless of the type of self-etching system. A solo irrigation with an EDTA/NaOCl solution resulted in a lower apical push-out strength compared with the other two experimental groups. [source] Effect of endodontic irrigation on bonding of resin cement to radicular dentinEUROPEAN JOURNAL OF ORAL SCIENCES, Issue 1 2005Mikako Hayashi The influence of endodontic irrigation on shear bond strengths of resin cement to radicular dentin was investigated. Human radicular dentin blocks were divided into four groups and subjected to one of four endodontic irrigations: ethylenediaminetetraacetic acid (EDTA) group, 17% EDTA for 60 s; EDTA/sodium hypochlorite (NaOCl) group, 17% EDTA for 60 s followed by 10 ml of 5% NaOCl for 15 s; NaOCl group, 10 ml of 5% NaOCl for 15 s; and control group, no treatment. Morphological changes of dentin surface after endodontic irrigation were observed by scanning electron microscopy (SEM). A resin block was bonded to the radicular dentin after irrigation using resin cement with either wet-bonding (Uni-Etch/One-Step; Bisco) or self-etching (Tyrian SPE/One-Step Plus; Bisco) adhesives. Shear bond strengths were measured and the penetration of resin tags into dentinal tubules at resin,dentin interface was observed by SEM. With the wet-bonding system, the shear bond strengths for the EDTA/NaOCl group, in which dentinal tubules openings and uniform resin tag penetration into dentinal tubules were observed, were significantly higher than the EDTA and control groups. With the self-etching system, the shear bond strengths were significantly lower in the EDTA group compared with the NaOCl and control groups. The effects of endodontic irrigation on the bonding of resin cement to radicular dentin depended on the dentin bonding system used. [source] Adhesion of a self-etching system to dental substrate prepared by Er:YAG laser or air abrasionJOURNAL OF BIOMEDICAL MATERIALS RESEARCH, Issue 2 2008Wanessa C. Souza-Zaroni Abstract The purpose of this study was to assess the microtensile bond strength of a self-etching adhesive system to enamel and dentin prepared by Er:YAG laser irradiation or air abrasion, as well as to evaluate the adhesive interfaces by scanning electron microscopy (SEM). For microtensile bond strength test, 80 third molars were randomly assigned to five groups: Group I, carbide bur, control (CB); II, air abrasion with standard tip (ST); III, air abrasion with supersonic tip (SP); IV, Er:YAG laser 250 mJ/4 Hz (L250); V, Er:YAG laser 300 mJ/4 Hz (L300). Each group was divided into two subgroups (n = 8) (enamel, E and dentin, D). E and D surfaces were treated with the self-etching system Adper Prompt L-Pop and composite buildups were done with Filtek Z-250. Sticks with a cross-sectional area of 0.8 mm2 (±0.2 mm2) were obtained and the bond strength tests were performed. Data were submitted to ANOVA and Tukey's test. For morphological analysis, disks of 30 third molars were restored, sectioned and prepared for SEM. Dentin presented the highest values of adhesion, differing from enamel. Laser and air-abrasion preparations were similar to enamel. Dentin air-abrasion with standard tip group showed higher bond strength results than Er:YAG-laser groups, however, air-abrasion and Er:YAG laser groups were similar to control group. SEM micrographs revealed that, for both enamel and dentin, the air-abrasion and laser preparations presented irregular adhesive interfaces, different from the ones prepared by rotary instrument. It was concluded that cavity preparations accomplished by both Er:YAG laser energies and air abrasion tips did not positively influence the adhesion to enamel and dentin. © 2007 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2008 [source] The effect of thermocycling and dentine pre-treatment on the durability of the bond between composite resin and dentineJOURNAL OF ORAL REHABILITATION, Issue 5 2004M. S. Huang Summary, The high bond strength between restorative resin and dentine plays an important role in long-term performance of restorations in the oral environment. A variety of treatment techniques have been described to enhance the bond strength of composite resin to dentine. Unfortunately, few studies have reported available bond durability of adhesive resins to dentine. The purpose of this research was to study the shear bond strength of composite resin to dentine pre-treated with phosphoric acid, self-etching agent or Nd:YAP laser irradiation. The durability of bond strength between resin and dentine stored in the artificial saliva thermocycling between 5 and 55 °C was also evaluated. The scanning electron microscope was used to assess the treated-dentine surfaces. The mean value of the shear bond strength in the acid-etching group (18·2 ± 4·9 MPa) was the highest among the three dentine treatments (self-etching system: 12·6 ±3·0 MPa, Nd:YAP laser: 13·4 ± 3·3 MPa) prior to thermocycling. After thermocycling, shear strength values of all treated dentines decreased with increasing number of the cycles. When subjected to 3000 thermocycles, the mean bond strengths of these pre-treated samples to composite resin became 9·1 ± 1·4, 7·8 ± 1·8, and 8·1 ± 1·7 MPa for acid-etching, self-etching and laser-irradiation, respectively, with a significant reduction of 38,50%. [source] Effect of post-space treatment on retention of fiber posts in different root regions using two self-etching systemsEUROPEAN JOURNAL OF ORAL SCIENCES, Issue 3 2008Ling Zhang The effect of post-space treatment on the retention of fiber posts in different root regions was evaluated using two self-etching systems. Post spaces were prepared in extracted premolars and then the root canals were subjected to one of the following post-space treatments: (i) water irrigation (control); (ii) etching with 35% phosphoric acid for 30 s; (iii) irrigation with 17% EDTA followed by 5.25% sodium hypochlorite (NaOCl); and (iv) ultrasonic agitation associated with 17% EDTA and 5.25% NaOCl irrigating solutions. The dentin surfaces were examined under scanning electron microscopy (SEM) after different post-space treatments. Fiber posts were then luted in the treated roots using resin cement with either Clearfil SE Bond or Clearfil DC Bond, and the thin-slice push-out test was performed. Scanning electron microscopy showed that all the post-space treatments tested were effective in removal of the smear layer of debris, or sealer/gutta-percha remnants, on the root canal. The apical push-out strength was affected by post-space treatment. Both 35% phosphoric acid etching and ultrasonic agitation in combination with EDTA/NaOCl irrigation improved the apical push-out strength of the fiber post, regardless of the type of self-etching system. A solo irrigation with an EDTA/NaOCl solution resulted in a lower apical push-out strength compared with the other two experimental groups. [source] Bond Strength of Two Resin Cements on Dentin Using Different Cementation StrategiesJOURNAL OF ESTHETIC AND RESTORATIVE DENTISTRY, Issue 4 2010RENATA MARQUES MELO MS ABSTRACT Purpose:, This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step "etch-and-rinse" technique. The null hypothesis was that the "etch-and-rinse" adhesive system would generate higher bond strengths than the self-etching adhesives. Materials and Methods:, Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 "etch-and-rinse" adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 × 5 × 4 mm), the specimens were stored in water (37°C, 24 hours), and sectioned to obtain beams (±1 mm2 of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (, = 0.05). Results:, Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The "etch-and-rinse" adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 ± 10.6; G4: 33.0 ± 8.9) compared to the self-etching adhesive systems (G1: 19.8 ± 6.6; G3: 17.8 ± 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used. Conclusion:, Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step "etch-and-rinse" adhesive resulted in significantly higher bond strength for both resin cements on dentin. CLINICAL SIGNIFICANCE Dual polymerized resin cements tested could deliver higher bond strength to dentin in combination with "etch-and-rinse" adhesive systems as opposed to their use in combination with self-etching adhesives. (J Esthet Restor Dent 22:262,269, 2010) [source] | ||||||||||