Home About us Contact
|
Home About us Contact | ||
|
|
||
Different Adhesive Systems (different + adhesive_system)
Selected AbstractsInfluence of whitening on the degree of conversion of dental adhesives on dentinEUROPEAN JOURNAL OF ORAL SCIENCES, Issue 3 2006Milena Cadenaro The aim of this study was to analyze the extent of polymerization of different adhesive systems on whitened dentin. One adhesive of each class was investigated: Adper Scotchbond Multi Purpose (3M ESPE); One-Step (Bisco); Clearfil Protect Bond (Kuraray); and Xeno III (Dentsply DeTrey). Dentin disks were treated with Opalescence Xtra Boost (Ultradent) for 30 min and bonded immediately after 24 h or after 14 d of storage in 100% humidity at 37°C. Unbleached dentin disks were prepared as controls. The extent of polymerization of bonded interfaces was obtained with differential scanning calorimetry (DSC) at 20, 40 and 60 s, and the data were statistically analyzed. The extent of polymerization obtained from DSC exotherms of adhesives applied immediately after whitening was significantly lower compared with controls. An increased extent of polymerization after storage was confirmed for all adhesives, and no difference with controls was found after 14 d. A prolonged irradiation time increased the curing rate for all the tested adhesives. This study supports the hypothesis that polymerization of the adhesive is reduced after dentin whitening and that delayed adhesive application reverses the polymerization inhibition. Prolonged polymerization intervals may counteract the inhibition of polymerization caused by the whitening procedure. Nevertheless, further in vivo studies should validate this issue. [source] Sealing capacity of a photochromatic flowable composite as protective base in nonvital dental bleachingINTERNATIONAL ENDODONTIC JOURNAL, Issue 3 2006C. Llena Abstract Aim, To evaluate microleakage of a flowable composite used as a protective isolating base, applied with different adhesive systems. Methodology, Seventy root-filled teeth were divided into seven groups. A flowable composite base (Tetric Flow Chroma) was used with three adhesive techniques (Syntac, Excite, Excite DCS; in the three cases with and without acid etching) and in a control group without dentine conditioning or adhesive placement. A 30% hydrogen peroxide solution was applied for 24 h in the pulp chambers, followed by the placement of a dye (silver nitrate) for 4 h. Each tooth was sectioned longitudinally, and examined under 4× magnification to assess the tooth/restoration dye leakage following a four-degree scale. Percentage of dye penetration was registered. Statistical analysis was made through the Tukey and Mann,Whitney U -tests. Results, Maximum leakage (100% of specimens) was recorded in the control group without an adhesive system. In the groups subjected to acid etching, the percentage of leakage corresponded to Excite DSC (10%), followed by Syntac (20%) and Excite (30%). In the groups in which only an adhesive system was used, 50% of the teeth demonstrated dye leakage. Statistically significant differences in terms of leakage were observed between the control group and the experimental groups (P < 0.05). There were no significant differences among the experimental groups, but comparing the leakage percentages obtained between the groups in which the teeth were subjected to prior acid etching, and those in which no etching was carried out, observed differences were significant (P = 0.04). Conclusions, There were no significant differences between the adhesive systems in terms of leakage. Acid etching significantly reduced leakage. [source] Microtensile bond strength of different adhesive systems in dentin irradiated with Er:YAG laserLASER PHYSICS LETTERS, Issue 7 2008L.M.G. Sierpinsky Abstract The objective this study was to evaluate in vitro the bond strength of two etch-and-rise and one self-etching adhesive system after dentin irradiation with Er:YAG (erbium: yttrium aluminum garnet) laser using microtensile test. The results revealed that the groups treated with laser Er:YAG presented less tensile bond strength, independently to the adhesive system used. The prompt L-pop adhesive presented less microtensile bond strength compared to the other adhesives evaluated. There was no difference between single bond and excite groups. The adhesive failures were predominant in all the experimental groups. The Er:YAG laser influenced negatively bond strength values of adhesive systems tested in dental substrate. (© 2008 by Astro Ltd., Published exclusively by WILEY-VCH Verlag GmbH & Co. KGaA) [source] Effect of sodium ascorbate on bond strength of different adhesive systems to NaOCl-treated dentinAUSTRALIAN ENDODONTIC JOURNAL, Issue 1 2010Cigdem Celik dds Abstract The aim of this study was to evaluate the effects of sodium ascorbate on bond strength of different adhesive systems to NaOCl-treated dentin. Eighty extracted molar teeth were used in the study. The buccal enamel surfaces were removed to obtain a flat dentin surface. The teeth were mounted in self-curing resin and dentin surfaces were irrigated with NaOCl for 10 min. Half of the specimens were treated with sodium ascorbate for 10 min. The teeth were randomly assigned to four subgroups according to the adhesive systems used (Clearfil SE Bond, Clearfil Tri-S Bond, Adper Prompt-L-Pop, Adper Single Bond 2). Bond strengths were determined with a Universal Testing Machine, at a crosshead speed of 0.5 mm/min. Data were statistically analysed using anova at a significance level of 0.05. Two-way anova revealed that the effect of sodium ascorbate application on bond strength of adhesive systems to NaOCl-treated dentin was statistically significant (P < 0.05). The bond strength results were significantly influenced by the application of sodium ascorbate (P < 0.05) and there was a significant difference between the adhesive systems (P < 0.05). Although statistically significant differences were not demonstrated in all adhesive resin groups, sodium ascorbate application after NaOCl treatment improved the bond strength values. [source] | ||||||||||