Home About us Contact
|
Home About us Contact | ||
|
|
||
Tubular Scaffold (tubular + scaffold)
Selected AbstractsElectrospun polylactide/silk fibroin,gelatin composite tubular scaffolds for small-diameter tissue engineering blood vesselsJOURNAL OF APPLIED POLYMER SCIENCE, Issue 4 2009Shudong Wang Abstract Many synthetic scaffolds have been used as vascular substitutes for clinical use. However, many of these scaffolds may not show suitable properties when they are exposed to physiologic vascular environments, and they may fail eventually because of some unexpected conditions. Electrospinning technology offers the potential for controlling the composition, structure, and mechanical properties of scaffolds. In this study, a tubular scaffold (inner diameter = 4.5 mm) composed of a polylactide (PLA) fiber outside layer and a silk fibroin (SF),gelatin fiber inner layer (PLA/SF,gelatin) was fabricated by electrospinning. The morphological, biomechanical, and biological properties of the composite scaffold were examined. The PLA/SF,gelatin composite tubular scaffold possessed a porous structure; the porosity of the scaffold reached 82 ± 2%. The composite scaffold achieved the appropriate breaking strength (1.28 ± 0.21 MPa) and adequate pliability (elasticity up to 41.11 ± 2.17% strain) and possessed a fine suture retention strength (1.07 ± 0.07 N). The burst pressure of the composite scaffold was 111.4 ± 2.6 kPa, which was much higher than the native vessels. A mitochondrial metabolic assay and scanning electron microscopy observations indicated that both 3T3 mouse fibroblasts and human umbilical vein endothelial cells grew and proliferated well on the composite scaffold in vitro after they were cultured for some days. The PLA/SF,gelatin composite tubular scaffolds presented appropriate characteristics to be considered as candidate scaffolds for blood vessel tissue engineering. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009 [source] Engineering of Vascular Grafts With Genetically Modified Bone Marrow Mesenchymal Stem Cells on Poly (Propylene Carbonate) GraftARTIFICIAL ORGANS, Issue 12 2006Jun Zhang Abstract:, Bone marrow mesenchymal stem cells (MSCs) have demonstrated their pluripotency to differentiate into different cell lineages and may be an alternative cell source for vascular tissue engineering. The objective of this study is to create small diameter vessels by seeding and culture of genetically modified MSCs onto a synthetic polymer scaffold produced by an electrospinning technique. A tubular scaffold (2 mm in diameter) with a microstructure of nonwoven fibers was produced by electrospinning of poly (propylene carbonate) (PPC). Rat MSCs obtained from bone marrow were expanded in culture and modified with vasculoprotective gene endothelial nitric oxide synthase (eNOS) or marker gene green fluorescent protein (GFP). These MSCs were seeded onto the electrospun fibrous grafts (internal diameter = 2 mm), and cultured in 5% CO2 at 37°C. The growth of MSCs in the scaffold was analyzed with scanning electron microscopy (SEM) and hematoxylin and eosin (H&E) staining. The gene transfer and transgenic gene expression were examined with fluorescence-activated cell sorting (FACS), immunochemical staining, reverse transcriptase-polymerase chain reaction (RT-PCR), and western blot. The production of nitric oxide (NO) by the engineered vessels was measured with an NO detection kit. Our data showed that the seeded cells integrated with the microfibers of the scaffold to form a three-dimensional cellular network, indicating a favorable interaction between this synthetic PPC scaffold with MSCs. High transduction efficiency was obtained with the use of concentrated retrovirus in the gene transfection of MSCs. The eNOS gene transcripts and protein were detected in the grafts seeded with eNOS-modified MSCs by RT-PCR and immunochemical staining. The amount of NO produced by grafts seeded with eNOS-modified MSCs was comparable to that produced by native blood vessels, and it was significantly higher than that in the grafts seeded with nonmodified MSCs. In summary, the vascular graft produced by culture of eNOS gene-modified MSCs onto the electrospun tubular scaffolds shows promising results in terms of function. The use of MSCs and therapeutic genes in tissue engineering of blood vessels could be helpful in improving vessel regeneration and patency. [source] A biomimetic tubular scaffold with spatially designed nanofibers of protein/PDS® bio-blends,BIOTECHNOLOGY & BIOENGINEERING, Issue 5 2009Vinoy Thomas Abstract Electrospun tubular conduit (4,mm inner diameter) based on blends of polydioxanone (PDS II®) and proteins such as gelatin and elastin having a spatially designed trilayer structure was prepared for arterial scaffolds. SEM analysis of scaffolds showed random nanofibrous morphology and well-interconnected pore network. Due to protein blending, the fiber diameter was reduced from 800,950,nm range to 300,500,nm range. Fourier-transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC) results confirmed the blended composition and crystallinity of fibers. Pure PDS scaffold under hydrated state exhibited a tensile strength of 5.61,±,0.42,MPa and a modulus of 17.11,±,1.13,MPa with a failure strain of 216.7,±,13%. The blending of PDS with elastin and gelatin has decreased the tensile properties. A trilayer tubular scaffold was fabricated by sequential electrospinning of blends of elastin/gelatin, PDS/elastin/gelatin, and PDS/gelatin (EG/PEG/PG) to mimic the complex matrix structure of native arteries. Under hydrated state, the trilayer conduit exhibited tensile properties (tensile strength of 1.77,±,0.2,MPa and elastic modulus of 5.74,±,3,MPa with a failure strain of 75.08,±,10%) comparable to those of native arteries. In vitro degradation studies for up to 30 days showed about 40% mass loss and increase in crystallinity due to the removal of proteins and "cleavage-induced crystallization" of PDS. Biotechnol. Bioeng. 2009; 104: 1025,1033. © 2009 Wiley Periodicals, Inc. [source] Windows of operation for bioreactor design for the controlled formation of tissue-engineered arteriesBIOTECHNOLOGY PROGRESS, Issue 3 2009Spyridon Gerontas Abstract The availability of large numbers of units of artificial arteries would offer significant benefits to the clinical management of bypass surgery. Tissue engineering offers the potential of providing vessels that can mimic the morphology, function, and physiological environment of native vessels. Ideally this would involve culturing stem cells in vitro within a biodegradable tubular scaffold so as to construct tissue for implantation. Essential to establishing a robust process for the production of tissue-engineered arteries is the understanding of the impact of changes in the operating conditions and bioreactor design on the construct formation. In this article, models of transport phenomena were developed to predict the critical flow rates and mass transfer requirements of a prototype bioreactor for the formation of tissue-engineered arteries. The impact of the cell concentration, tube geometry, oxygen effective diffusivity in alginate, substrate and metabolite concentration levels, feed rate, and recycle rate on the design of the bioreactor was visualized using windows of operation and contour plots. The result of this analysis determined the best configuration of the bioreactor that meets the cellular transport requirements as well as being reliable in performance while seeking to reduce the amount of nutrients to be used. © 2009 American Institute of Chemical Engineers Biotechnol. Prog., 2009 [source] Electrospun polylactide/silk fibroin,gelatin composite tubular scaffolds for small-diameter tissue engineering blood vesselsJOURNAL OF APPLIED POLYMER SCIENCE, Issue 4 2009Shudong Wang Abstract Many synthetic scaffolds have been used as vascular substitutes for clinical use. However, many of these scaffolds may not show suitable properties when they are exposed to physiologic vascular environments, and they may fail eventually because of some unexpected conditions. Electrospinning technology offers the potential for controlling the composition, structure, and mechanical properties of scaffolds. In this study, a tubular scaffold (inner diameter = 4.5 mm) composed of a polylactide (PLA) fiber outside layer and a silk fibroin (SF),gelatin fiber inner layer (PLA/SF,gelatin) was fabricated by electrospinning. The morphological, biomechanical, and biological properties of the composite scaffold were examined. The PLA/SF,gelatin composite tubular scaffold possessed a porous structure; the porosity of the scaffold reached 82 ± 2%. The composite scaffold achieved the appropriate breaking strength (1.28 ± 0.21 MPa) and adequate pliability (elasticity up to 41.11 ± 2.17% strain) and possessed a fine suture retention strength (1.07 ± 0.07 N). The burst pressure of the composite scaffold was 111.4 ± 2.6 kPa, which was much higher than the native vessels. A mitochondrial metabolic assay and scanning electron microscopy observations indicated that both 3T3 mouse fibroblasts and human umbilical vein endothelial cells grew and proliferated well on the composite scaffold in vitro after they were cultured for some days. The PLA/SF,gelatin composite tubular scaffolds presented appropriate characteristics to be considered as candidate scaffolds for blood vessel tissue engineering. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009 [source] | ||||||||||