Home About us Contact
|
Home About us Contact | ||
|
|
||
Izod Impact Strength (izod + impact_strength)
Selected AbstractsEnhanced compatibility of PA6/POE blends by POE- g -MAH prepared through ultrasound-assisted extrusionJOURNAL OF APPLIED POLYMER SCIENCE, Issue 3 2010Tingting Xie Abstract The effects of POE- g -MAH, prepared through different methods, on morphology and properties of PA6/POE/POE- g -MAH blends are summarized in this article. The grafting degree of POE- g -MAH can be increased through the ultrasound-assisted extrusion. Experimental results showed that the addition of POE- g -MAH can increase the mechanical properties of the PA6/POE blend and decrease the particle size of POE dispersed phase in PA6 matrix due to the compatibilization by POE- g -MAH. The PA6/POE blend compatibilized by POE- g -MAH prepared through the ultrasound-assisted extrusion has smaller particle size of POE dispersed phase and higher notched Izod impact strength than that by POE- g -MAH with similar grafting degree initiated only by peroxide. This result is ascribed to some anhydride rings attached to the chain terminus of POE due to ultrasound initiation. Rheological and Molau test results also showed enhanced compatibilization of POE- g -MAH prepared through the ultrasound-assisted extrusion on the PA6/POE blend due to a structural difference of POE- g -MAH. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010 [source] Mechanical and thermal properties of polypropylene/sugarcane Bagasse compositesJOURNAL OF APPLIED POLYMER SCIENCE, Issue 6 2007B. Ramaraj Abstract To determine the possibility of using sugarcane bagasse (SCB) waste as reinforcing filler in the thermoplastic polymer matrix, SCB-reinforced polypropylene (PP) composites were prepared. The PP and SCB composites were prepared by the extrusion of PP resin with 5, 10, 15, and 20 wt % of SCB filler in a corotating twin screw extruder. The extruded strands were cut into pellets and injection molded to make test specimens. These specimens were tested for physicomechanical properties such as tensile, flexural, Izod, and Charpy impact strengths, density, water absorption, and thermal characteristics, namely, heat deflection temperature (HDT), melt flow index, and thermogravimetric analysis. It was found that the flexural strength increased from 23.66 to 26.84 MPa, Izod impact strength increased from 10.499 to 13.23 Kg cm/cm, Charpy impact strength increased from 10.096 to 13.98 Kg cm/cm, and HDT increased from 45.5 to 66.5°C, with increase in filler loading from 5 to 20% in the PP matrix. However, the tensile strength and elongation decreased from 32.22 to 27.21 MPa and 164.4 to 11.20% respectively. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3827,3832, 2007 [source] Effect of EPDM on Morphology, Mechanical Properties, Crystallization Behavior and Viscoelastic Properties of iPP+HDPE BlendsMACROMOLECULAR SYMPOSIA, Issue 1 2007Nina Vranjes Abstract Summary: Blends of isotactic polypropylene (iPP) and high density polyethylene (HDPE) with and without ethylene-propylene-diene (EPDM) terpolymer as compatibilizer were systematically investigated to determine the influence of the EPDM on blends properties. The morphology was studied by Scanning Electron Microscopy (SEM). Mechanical properties of investigated systems: tensile strength at break, elongation at break, yield stress and Izod impact strength were determined. Crystallization behavior was determined by Differential Scanning Calorimetry (DSC). Dynamic Mechanical Analysis (DMA) was used to determined the storage modulus (E,), loss modulus (E,), and loss tangent (tan ,). The PP+HDPE blend revealed poor adhesion between PP and HDPE phases. Finer morphology was obtained by EPDM addition in PP+HDPE blends and better interfacial adhesion. Addition of HDPE to PP decreased tensile strength at break, elongation and yield stress. Decrease of tensile strength and yield stress is faster with EPDM addition in PP+HDPE blends. Elongation at break and impact strength was significantly increased with EPDM addition. The addition of EPDM in PP+HDPE blends did not significantly change melting points of PP phase, while melting points of HDPE phase was slightly decreased in PP+HDPE+EPDM blends. The EPDM addition increased the percentage of crystallization (Xc) of PP in PP+HDPE blends. The increase of Xc of HDPE was found in the blend with HDPE as matrix. Dynamical mechanical analysis showed glass transitions of PP and HDPE phase, as well as the relaxation transitions of their crystalline phase. By addition of EPDM glass transitions (Tg) of HDPE and PP phases in PP+HDPE blends decreased. Storage modulus (E,) vs. temperatures (T) curves are in the region between E,/T curves of neat PP and HDPE. The decrease of E, values at 25,°C with EPDM addition in PP+HDPE blends is more pronounced. [source] The effect of polyoxypropylene-montmorillonite intercalates on polymethylmethacrylatePOLYMER COMPOSITES, Issue 1 2009Nehal Salahuddin Polymethylmethacrylate (PMMA)-layered silicate nanocomposites have been prepared by in situ polymerization of commercial type of methylmethacrylate monomer (MMA), for denture base material, into organoclay. Organoclay was prepared through an ion exchange process between sodium cations in montmorillonite and NH3+ groups in polyethertriamine hydrochloride and polyoxypropylene triamine hydrochloride with different molecular weight (5000, 440). X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) have been used to investigate the structure of the resulting composites. Both intercalated and exfoliated nanocomposites were obtained depending on the type and amount of organoclay. The thermal decomposition temperatures of the nanocomposites were found to be higher than that of pristine polymer. PMMA was strongly fixed to inorganic surfaces, due to cooperative formation of electrostatic bonding between NH3+ group and negatively charged surface of layered silicate and amide linkage between PMMA and polyethertriamine or polyoxypropylene triamine. The effect of the organoclay on the hardness, toughness, tensile stress, and elongation at break of the polymer was studied and was compared with pristine polymer. The hardness and Izod impact strength of PMMA-organoclay nanocomposites were enhanced with the inclusion of clay. Tensile properties appear to be enhanced at certain organoclay content. However, the water absorption is slightly higher than the pristine PMMA. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers [source] Morphology and mechanical properties of impact modified polypropylene blendsPOLYMER ENGINEERING & SCIENCE, Issue 11 2008Nathan Tortorella Isotactic polypropylene (PP) has been reactively blended with various grades of an ethylene,octene copolymer (EOC) in a twin-screw extruder. Free radical polymerization of styrene and a multifunctional acrylate during melt extrusion has resulted in an enhancement of mechanical properties over the binary blend. The reactive blend exhibits a notched Izod impact strength over 12 times that of pure polypropylene and greater than double the performance of the binary blend. Electron microscopy shows that by grafting onto the polymers, elastomer particle size and interparticle distance decrease, while particle shape becomes less spherical. The acrylate is crucial to achieve superior performance, as infrared spectra correlate an increase in graft yield to improvements in stress,strain behavior and impact strength. In addition, melt flow index (MFI) and melt strength data indicate a reduction in unwanted side reactions of polypropylene and the presence of long-chain branching. Dynamic-mechanical analysis reveals that the reaction promotes miscibility between polypropylene and the EOC and reduces molecular mobility at their glass-transition temperatures. Mechanical properties, graft yield, and MFI are shown to be highly dependent upon the elastomer's concentration, density, and molecular weight, initiator and monomer concentration, as well as processing temperature. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers [source] | ||||||||||